10mic/12mic/15mic Simultaneously BOPA Film (nylon film) for Packaging and Lamination

10mic/12mic/15mic Simultaneously BOPA Film (nylon film) for Packaging and Lamination

BOPA nylon film for printing and lamination Specification: Characteristics: 1.Excellent resistance to puncture and abras;
Basic Info.
Roll Width 300mm-2, 000mm (Customized Welcomed)
Transport Package in Pallet
Specification pallet
Trademark no
Origin China
HS Code 3920920000
Production Capacity 1000ton/Month
Product Description

BOPA nylon film for printing and lamination

Specification:

Thickness (μm)

Width (mm)

Roll Diameter (mm)

12, 15

300-2000

300-610

Characteristics:

1.Excellent resistance to puncture and abrasion.

2.Wide temperature use range (-600C ~1500C).

3.Good barrier against oxygen, nitrogen, carbon dioxide and odor.

4.Resistant to acid, alkaline, grease and different kinds of common organic solvent.

5.High transparency and gloss.

Typical Physical Properties:

Items

Test Methods

Units

Typical Value

Type

--

--

BOA

TOA-C

OA-1

Thickness

GB 6672

μm

15

15

15

Density

GB 1033

g/cm3

1.14

1.14

1.14

Tensile Strength (MD/TD)

GB 13022

MPa

230/235

230/265

235/300

Elongation at Break (MD/TD)

GB 13022

%

95/85

128/85

125/90

Heat Shrinkage (MD/TD)

GB 12026

(1600C × 5min)

%

1.3/0.8

1.0/1.2

1.3/1.6

Surface Tension

GB/T 14216

mN/m

60

60

58

Haze

GB 2410

%

1.0

2.8

2.8

Oxygen Permeability

GB 1038

cm3/(m2 .24h.atm)

30

30

30

Notes: MD: Machine Direction; TD: Transverse Direction.

The above data can only be regarded as typical physical properties, not guarantee values.

Application

Type of BOA,TOA-C and OA-1 can be applied in the process of printing and laminating, TOA-S and OA-2 in laminating without printing. BOPA films are humidity sensitive, which may cause printing or laminating defect in high humidity absorption and impacting the usage satisfaction, thence, users are recommended to process the unpacked film rolls quickly, pack the printed films with aluminum metallized films, and laminate them without delay. To obtain product's good quality, BOPA is not suggested to be processed in the humidity over 75%RH.

Usage Examples

BOPA (15μm) / EVA (50μm) (or PE 50-60μm)

Ham, sausage

PET (12μm) // AL (7~9μm) // BOPA(15μm) // CPP (60~70μm)

Fired chicken

K-OPA (15μM) // PE (40~60μm)

Dried fish

BOPA (15μm) // PE (40μm)

Sea food

BOPA 15μm // PE (60-100μm)

Refined rice

K-OPA 15μm //EVA 50μm

Bean sauce

BOPA (15μm) // PE (60μm)& BOPA (15μm) // AL (7~9μm) //CPP (40~60μm)

Pickle

BOPA (15μm) //VM-PET (12μm)&VM-OPP (20μm) //PE (60μm)

Tea

BOPA (15μm) //VM-PET (12μm)& VM-OPP (20μm) //EVA (60μm)

Capsicol

10mic/12mic/15mic Simultaneously BOPA Film (nylon film) for Packaging and Lamination


10mic/12mic/15mic Simultaneously BOPA Film (nylon film) for Packaging and Lamination


10mic/12mic/15mic Simultaneously BOPA Film (nylon film) for Packaging and Lamination


10mic/12mic/15mic Simultaneously BOPA Film (nylon film) for Packaging and Lamination


10mic/12mic/15mic Simultaneously BOPA Film (nylon film) for Packaging and Lamination




Industrial Standards:

<Biaxially Oriented polyamide (nylon) Film> China National Standard

(Standard Code: GB/T 20218-2006)

Transportation and Storage Notices:

Any impact or collision during transporting, loading and unloading may result in the damage of roll surface and edge. Storage in shady, cool and dry condition avoiding direct sunshine and rain is recommended.

Send inquiry